Heat stabilized series
Heat stabilized series
Product description:Roilon Polyamide engineering plastics heat stabilized series is modified with high efficiency heat stabilized additives which improved the long term working temperature of the material.This series contained glass fiber filled grades and unfilled grades.It is suitable for the applications work under higher temperatures, especially automotive parts.
Product Specification:
| Grade Name | A3H | A3G6H | A3G7H | A3G8H | A3G10H | A3M6H | A3MG8H | A3M8H | ||
| Performance | Standard | Unit | PA66 Unfilled | PA66 + 30%GF | PA66 + 35%GF | P66 + 40%GF | PA66 + 50%GF | PA66 + 30%MD | PA66+40% (GF+MD) | PA66 + 40%MD |
| Physical properties | | | | | | | | | | |
| Density | ISO 1183 | g/cm3 | 1.14 | 1.36 | 1.41 | 1.46 | 1.56 | 1.36 | 1.47 | 1.47 |
| Melting point | ISO 11357 | °C | 260 | 260 | 260 | 260 | 260 | 260 | 260 | 260 |
| Shrinkage (latitude) | ISO 294-4 | % | 1.9 | 0.5 | 0.4 | 0.3 | 0.3 | 0.7 | 0.6 | 0.6 |
| Shrinkage(longitude) | ISO 294-4 | % | 1.9 | 0.8 | 0.7 | 0.6 | 0.5 | 0.7 | 0.9 | 0.6 |
| Mechanical Properties | | | | | | | | | | |
| Tensile Modulus | ISO 527 | MPa | 3000 | 10000 | 11000 | 11500 | 16000 | 7700 | 10000 | 7600 |
| Tensile Strength | ISO 527 | MPa | 85 | 195 | 200 | 205 | 240 | 190 | 135 | 190 |
| Elongation | ISO 527 | % | 20 | 3 | 3 | 2.5 | 2 | 1 | 2 | 1 |
| Flexure Modulus | ISO 178 | MPa | 2900 | 9200 | 9500 | 10000 | 13500 | 7000 | 9000 | 6800 |
| Impact Strength (notched) | ISO 179/1eA | kJ/m2 | 4 | 11 | 13 | 12 | 15 | 3 | 4 | 2 |
| Impact Strength (Unnotched) | ISO 179/1eU | kJ/m2 | NB | 80 | 90 | 90 | 95 | 45 | 43 | 40 |
| Heat properties | | | | | | | | | | |
| HDT(1.80 MPa) | ISO 75 | °C | 75 | 253 | 255 | 255 | 255 | 232 | 240 | 232 |
| Grade Name | B3G6H | B3G8H | B3G10HU | B3G12HU | B3MG6H | B3MG9H | C3G6HU | ||
| Performance | Standard | Unit | PA6 + 30%GF | PA6 + 40%GF | PA6+50%GF | PA6+60%GF UV Stabilized | PA6+30% (MD+GF) | PA6+45% (MD+GF) | PA6/66+30%GF |
| Physical properties | | | | | | | | | |
| Density | ISO 1183 | g/cm3 | 1.35 | 1.45 | 1.55 | 1.65 | 1.35 | 1.52 | 1.35 |
| Melting point | ISO 11357 | °C | 220 | 220 | 220 | 220 | 220 | 220 | 245 |
| Shrinkage (Latitude) | ISO 294-4 | % | 0.3 | 0.2 | 0.1 | 0.1 | 0.5 | 0.3 | 0.4 |
| Shrinkage (Logitude) | ISO 294-4 | % | 0.7 | 0.6 | 0.4 | 0.2 | 0.8 | 0.5 | 0.7 |
| Mechanical Properties | | | | | | | | | |
| Tensile Modulus | ISO 527 | MPa | 9500 | 13000 | 14500 | 20000 | 7500 | 10000 | 9500 |
| Tensile Strength | ISO 527 | MPa | 195 | 210 | 220 | 240 | 97 | 130 | 185 |
| Elongation | ISO 527 | % | 3.5 | 3 | 2.5 | 2 | 3 | 2 | 3 |
| Flexure Modulus | ISO 178 | MPa | 8500 | 12800 | 14000 | 18000 | 7000 | 9000 | 8600 |
| Impact Strength (Notched) | ISO 179/1eA | kJ/m2 | 15 | 19 | 18 | 15 | 13 | 6 | 12 |
| Impact Strength (Unnotched) | ISO 179/1eU | kJ/m2 | 95 | 105 | 100 | 85 | 60 | 40 | 83 |
| Heat properties | | | | | | | | | |
| HDT(1.80 MPa) | ISO 75 | °C | 205 | 210 | 216 | 215 | 205 | 210 | 230 |
Roilon material complied with ROHS and REACH
Typical applications:
| | Application:Rocker cover Material selection: RoilonTMA3G7H,A3MG8HandA3M8H, |
| | |
| | Application:Engine cover Material Selection: RoilonTMB3MG6HandB3MG9H |
| | |
| | Application:Water Tank Material selection: RoilonTMA3G6HandA3G7H |